ABSTRACT
Abstract The aim of this study was to evaluate the Streptococcus mutans biofilm influence on the roughness (Ra), gloss (GU), surface hardness (KHN) and flexural strength (FS) of high viscosity bulk fill composites. Filtek Bulk Fill (FBF), Tetric N Ceram Bulk Fill (TNC), X-tra fil Bulk Fill (XF) and Filtek Z350 (FZ) were used. Ten discs of each composite were prepared for Ra, KHN and GU and 20 bars for the FS. After 24 h, specimens were polished and initial analyzes performed. Samples were sterilized and subjected to biodegradation for 7 days and final analyzes performed. Representative samples of each group were evaluated in Scanning Electron Microscope. Data were submitted to ANOVA two factors and Tukey test. XF presented the highest values (p<0.05) of Ra before and after biodegradation (0.1251; 0.3100), and FZ (0.1443) the lowest after biodegradation (p<0.05). The highest GU values (p<0.05) were observed for FZ (71.7; 62) and FBF (69.0; 64.6), and the lowest (p<0.05) for TNC (61.4; 53.3) and XF (58.5; 53.5), both before and after biodegradation. For KHN the highest values were obtained by XF (151.7; 106), and the (p< 0.05) lowest values for TNC (62.2; 51.8), both before and after biodegradation. The highest values (p<0.05) of FS were observed for FZ (127.6) and the lowest (p<0.05) for TNC (86.9); after biodegradation, XF (117.7) presented the highest (p<0.05) values compared to TNC and FZ." In conclusion, biodegradation increased Ra and decreased GU and KHN for all. Concerning FS, degradation provided a significant decreased value only for FZ.
Resumo O objetivo deste estudo foi avaliar a influência do biofilme de S. mutans na rugosidade (Ra), brilho (GU), dureza superficial (KHN) e resistência à flexão (FS) de compósitos de Bulk Fill de alta viscosidade. Foram utilizados Filtek Bulk Fill (FBF), Tetric N Ceram Bulk Fill (TNC), X-tra fil Bulk Fill (XF) e Filtek Z350 (FZ). Dez discos de cada compósito foram preparados para Ra, KHN e GU e 20 barras para o FS. Após 24 h, os espécimes foram polidos e as análises iniciais realizadas. As amostras foram esterilizadas e submetidas a biodegradação por 7 dias e as análises finais foram realizadas. Amostras representativas de cada grupo foram avaliadas no Microscópio Eletrônico de Varredura. Os dados foram submetidos à ANOVA dois fatores e teste de Tukey. XF apresentou os maiores valores (p<0,05) de Ra antes e após a biodegradação (0,1251; o00,3100) e FZ (0,1443) os menores após a biodegradação (p<0,05). Os maiores valores de GU (p<0,05) foram observados para FZ (71,7; 62) e FBF (69,0; 64,6), e os mais baixos (p<0,05) para TNC (61,4; 53,3) e XF (58,5; 53,5), ambos antes e depois da biodegradação. Para KHN, os valores mais altos foram obtidos por XF (151,7; 106), e os (p<0,05) valores mais baixos para TNC (62,2; 51,8), antes e depois da biodegradação. Os maiores valores (p <0,05) de FS foram observados para a FZ (127,6) e os menores (p<0,05) para a TNC (86,9); após biodegradação, o XF (117,7) apresentou os maiores valores (p<0,05) em comparação ao TNC e FZ. Em conclusão, a biodegradação aumentou o Ra e diminuiu a GU e a KHN para todos. Em relação à FS, a degradação promoveu uma diminuição significativa apenas para a FZ.
Subject(s)
Streptococcus mutans , Flexural Strength , Surface Properties , Materials Testing , HardnessABSTRACT
Abstract This study evaluated gloss and color changes of esthetic restorative materials subjected to different acidic beverages. Specimens of resin composites (Z350XT (Z350), IPS Empress Direct (ED), Charisma Diamond (CD)) were prepared and the initial surface gloss and color (ΔE) were measured (n=10). Then, the specimens were immersed in 4 mL of each of the different beverages (cranberry juice; Coca-Cola; coffee or artificial saliva) during 15 min, 3x/day for 14 days and new gloss and color readings were obtained. Color change was evaluated with the ΔE formula and gloss change values were obtained by the formula: (final gloss - initial gloss). Data was submitted to two-way ANOVA followed by Tukey's post hoc test (a=0.05). CD showed the lowest color change among resin composites. The highest ΔE values were obtained after immersion in coffee and cranberry juice. Coffee promoted the highest gloss change (worst gloss retention), followed by cranberry juice, Coca-cola and artificial saliva (p<0.05). The type of beverage significantly influenced the gloss of resin composites. Coca-cola reduced gloss of the three resin composites in a similar manner. Coffee affected the ED gloss more than that of Z350 and CD, while cranberry juice affected Z350 more than ED and CD. Saliva had a more pronounced effect on the gloss retention of CD than ED. The beverages used in this study influenced the optical surface properties of the composites studied.
Resumo O objetivo foi avaliar as alterações de brilho e cor de materiais restauradores estéticos submetidos ao armazenamento em diferentes bebidas ácidas. Foram preparados espécimes de compósitos de resina (Z350XT (Z350), IPS Empress Direct (ED), Charisma Diamond (CD) e o brilho e a cor (ΔE) de superfície mensurados (n=10). Em seguida, os espécimes foram imersos em 4 mL de cada uma das diferentes bebidas (suco cranberry, Coca-Cola, café, ou saliva artificial) durante 15 min, 3x/dia durante 14 dias e o brilho e a cor novamente mensurados. A alteração de cor foi avaliada pela fórmula ΔE e os valores de alteração de brilho foram obtidos pela fórmula: (brilho final - brilho inicial). Os dados foram submetidos à ANOVA e Tukey (a = 0,05). CD apresentou menor alteração de cor quando comparado aos demais compósitos e maiores valores de ΔE foram obtidos após imersão em suco de café e cranberry. O café promoveu maior perda de brilho, seguido pelo suco cranberry, Coca-cola e saliva artificial (p <0,05). O tipo de bebida influenciou significativamente no brilho dos compósitos resinosos. Coca-cola reduziu o brilho dos três compósitos de maneira similar. O café promoveu maior alteração do brilho do ED, quando comparado ao Z350 e CD, enquanto o suco de cranberry afetou mais o Z350 do que o ED e o CD. A saliva teve efeito mais significativo na perda do brilho do CD do que o ED. As bebidas utilizadas neste estudo influenciaram as propriedades ópticas de superfície dos compósitos.